Hot dipped galvanized wire production line

Hot-dip galvanized wire is divided into ordinary hot-dip galvanized, high-zinc, zinc-aluminum alloy wire, and the wire diameter is usually 1.6-4.5 mm.
The production line adopts the following production process:
I-wheel pay-off → straightening device → heat treatment annealing furnace → water washing tank → smokeless pickling tank → hot water washing tank → boosting tank → drying furnace → galvanizing pot → wiping → cooling → boosting tank → drying Furnace → hot-dip Galfan pot → wipe → cool → vertical wire take-up machine
It can realize the production of ordinary zinc, high zinc, zinc aluminum alloy wire, low carbon steel wire and high carbon steel wire on the same production line.
Hot-dip galvanizing is immersion plating in a molten zinc solution. The production speed is fast, and the coating is thick but uneven. The minimum thickness allowed by the market is 45 microns, and the maximum can reach more than 300 microns. The color is darker, consumes a lot of zinc metal, forms an infiltration layer with the base metal, and has good corrosion resistance. Hot-dip galvanizing can be maintained for decades in outdoor environments.
Since the resulting coating is thicker, hot-dip galvanizing has better protective properties than electro-galvanizing, so it is an important protective coating for steel parts used in harsh working environments. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, ocean exploration, metal structure, power transmission, shipbuilding and other industries. In agricultural fields such as pesticide irrigation, greenhouses, and construction industries such as water and gas transmission, wire casing, scaffolding, and bridges , Highway guardrails, etc., have been widely used in recent years.
Q:What information should i give to you to make proposal?
A:(1).Material:low carbon or high carbon
(2)Capacity:tons/month
(3)Wire diameter:mm
(4)Zinc coat thickness:g/m2
(5)Wire usage:for which application
(6)Energy:natural gas,LPG,electricity?
(7)Workshop size:L*W
(8)Industrial voltage/frequency